Dimensions of sheets – AKRILIKA STONE, KRISTALL

Collection Thickness, mm Length, mm Width, mm Weight, kg
Akrilika Stone, Kristall 12,3 3660 760 60-65

TECHNICAL DATA – PERFORMANCE PROPERTIES OF PRODUCT – AKRILIKA STONE, KRISTALL

1. Physical and mechanical properties

Property Result Test method *
Density 1,74 g / cm3 ASTM D792-13 (A) 1
Flexural strength 64,9 MPa ASTM D790-15 (A) 1
Flexural modulus 11975 MPa ASTM D790-15 (A) 1
Tensile elongation 0,66% ASTM D638-14 1
Tensile strength 45,6 MPa ASTM D638-14 1
Tensile modulus 9840 MPa ASTM D638-14 1
Barcol Hardness 68 ASTM D2583-13a 1

2. Using properties

Property Result Test method *
Fire classification B / s-1 (EN 13501-1+A1.2009) ISO 9239-1:2010, ISO 11925-2:2010 3
Class 1 (AC: 2014) BS 476-7: 1997 4
Lighttest pass (>6 ) DIN EN 15187 (Blue wool sc) 2
pass (>6 ) ISO 105-B02:2014 (Blue wool sc) 1
Resistance to impact pass (no change till 25N ) DIN EN 438- 2 2
pass (no changes 0,87m /7.7 N) ASTM D5420-1 1
Resistance to impact (small & large ball) Class IC2 (F-12N / H-1,6m) EN 13329-F: 2009 3
Temperature resistance no changes ( 4 h / 75°C) AMK Merkblatt 001, 3.3 2
High temperature resistance no changes ( 24 h / hot wax) NEMA LD 3: 2005 -3.6 1
Humid climate resistance no changes (14 Days, 40°C, 85% H) 2 PfG 2507 – 1 2
Alternating climate resistance no changes (-20°C – +60°C) 2 PfG 2507 – 2 2
Dimension deviation 1,33 mm / m pass (max 1,50 mm/m) 2 PfG 2507 – 2 2
Behaviour in dry heat Class 7A 180°C (DIN 68861- 7, 2001-04 ) DIN EN 12722 2
Behaviour in wet heat Class 8A 100°C (DIN 68861-8, 2001-04 ) DIN EN 12721 2
Boiling water resistance no changes NEMA LD 3: 2005 -3.5 1
Vapourization with water no changes AMK MB-005.1 2015 2
Water absorption pass (Immersion 0,27% 49 Days, 23°C Water) ASTM D570-98 (2010) 1
Abrasion resistance Class 2A > 650 rotations ( DIN 68861-2, 2013-02) DIN EN 15185 2
Graphite test no changes (Test with pencil 6HB) DIN EN 12720 2
Cigarette test pass ANSI Z124-3 2005. 5.4 1

1 SGS-CSTC – Test report GZIN160200187CCM dtd 2016
2 TÜV Rheinland – Test report 21255144_001 dtd 2016
3 TÜV Rheinland – Test report 21245130_001 dtd 2016
4 SGS-CSTC – Test report GZIN160200190CCM dtd 2016

BEHAVIOUR AT CHEMICAL INFLUENCE – AKRILIKA STONE, KRISTALL

3. Test according to DIN 68861-11

Test substrates / Requirements acc. DIN EN 12720
Reagents 1 Cl 1A -MAX 1B 1C-MIN Results /
Acetic acid 16h 5 1h 5 1A5 ok
Citric acid 16h 5 1h 5 1A5 ok
Ammonia water 16h 5 2min 5 1A5 ok
Ethylene alcohol 16h 5 1h 4 1A5 ok
Red wine 16h 5 6h 5 10min 5 1A5 ok
Beer 16h 5 6h 5 10min 5 1A5 ok
Cola beverage 16h 5 16h 5 10min 5 1A5 ok
Coffee 16h 5 16h 5 10min 5 1C5-1A5 ok
Black tea 16h 5 16h 5 10min 5 1B5-1A5 ok
Black current juice 16h 5 16h 5 10min 5 1A5 ok
Condensed milk 16h 5 16h 5 10min 5 1C5-1A5 ok
Petrol 16h 5 2min 5 1A5 ok
Acetone 16h 5 10s 2 1A3-1A4 ok
Ethylen-butylene acetate 16h 5 10s 2 1A3-1A4 ok
Olive oil 16h 5 16h 5 1A5 ok
Mustard 16h 5 6h 5 1B5-1A5 ok
Disinfectant 16h 5 10min 5 2min 5 1A5 ok
Black ballpoint ink 16h 5 1A2 ok
Stamp pad ink 16h 5 1A3 ok
Detergent 16h 5 1h 5 1A5 ok
Detergent solution 16h 5 1h 5 2min 5 1A5 ok

5 – no change, 4 – minor change, 3-moderate change, 2- significant change
1 TÜV Rheinland – Test report 21255144_000 dtd 2016

4. Test according to ISO 19712-2:2007 p102

Test substrates Requirements acc. ISO 19712-2 p10 (A)
MAX NORM MIN Results /
Coffee 5 4 3 4 ok
Natronlauge, 25% 5 4 3 5 ok
H-peroxid, 30% 5 4 3 5 ok
Acetone 5 4 3 3 ok
Black shoe polish 5 4 3 4 ok
Citric acid, 10% 5 4 3 5 ok

2 TÜV Rheinland – Test report 21245130_001 dtd 2016

5. Test according to ANSI Z124.3-20053

Stain resistance Requirements acc. ANSI Z124.3-2005
Test substrates T MAX-MIN max depth Results
Black crayon 16h 1 5 0,127mm 1 1 0 mm pass
Black shoe polish 16h 1 5 0,127mm 1 1 0 mm pass
Blue washable ink 16h 1 5 0,127mm 5 5 0,03 mm pass
Gentian violet solution 16h 1 5 0,127mm 5 5 0,111 mm pass
Iodine solution, 1% 16h 1 5 0,127mm 2 3 0 mm pass
Lipstick 16h 1 5 0,127mm 1 1 0 mm pass
Hair dye 16h 1 5 0,127mm 5 5 0,1 mm pass
Chemical resistance Requirements acc. / ANSI Z124.3-2005
Test substrates T Results
Naphtha 16h no changes pass
Ethyl alcohol 16h no changes pass
Amyl acetate 16h superficial surface changes pass
Ammonia solution, 10% 16h no changes pass
Citric acid, 10% 16h no changes pass
Urea, 6% 16h no changes pass
Hydrogen peroxide solution, 3% 16h no changes pass
Concentr. sodium hypochlorite solution 16h no changes pass

3 SGS-CSTC – Test report GZIN160200187CCM dtd 2016

FOOD SAFETY TESTS AND CERTIFICATES – AKRILIKA STONE, KRISTALL

6. Food safety tests

Test Results Norms *
Sensory analysis, smell/taste
(H2O)
pass LFGB, § 31-1, DIN 10955
Reg EU 1935/2014 -3.
1
Migration of Acrylonitril, formaldehyde, Metals (Ba, Co, Cu, Fe, Li, Mn, Zn), PAA, PAHs, 8 EU-PAHs, acrylic and methacrylic acid pass Reg EU 10/2011
Reg EU 1907/2006
DIN EN 13130
1
Color migration of pigmented plastics pass BfR-IX, Resolution AP (89) 1 1
Metal laxness pass BDIN EN 1388-1 2

1 TÜV Rheinland – Test report 0003162423/40 AZ227041 dtd 2016
2 NIH Poland – Test report 038/106/16/LHZ/D dtd 2016

7. Certificates of Polish National Institute of Hygiene

Certificate of health quality H-HZ-6071-179/16/D dtd 2016
Hygienic Certificate HK/B/080401/2016 dtd 2016
Radiation Hygienic Certificate HR/B/56/2016 dtd 2016

TECHNICAL DATA – PERFORMANCE PROPERTIES OF PRODUCT – APIETRA

Dimensions of sheets

Collection Thickness, mm Length, mm Width, mm Weight, kg
Apietra 12,3 3660 760 60-65
Apietra 6 2440 760 20-23

1. Physical and mechanical properties

Property Result Test method *
Density 1,72 g / cm3 ASTM D792-13 (A) 6
Flexural strength 54,9 MPa ASTM D790-15 (A) 1
Flexural modulus 9680 MPa ASTM D790-15 (A) 1
Barcol Hardness 66 ASTM D2583-13a 1

2. Using properties

Property Result Test method *
Fire classification B / s-1 (EN 13501-1+A1.2009) ISO 9239-1:2010, ISO 11925-2:2010 3
pass (Oxygen index 41.6) JC 908-2002 s. 6.7.2. 4
Lighttest pass (>6 ) DIN EN 15187 (Blue wool sc) 5
pass < 2 CIE GB/T 11942-89 4
Resistance to impact pass (no change till 25N ) DIN EN 438- 2 2
pass JC 908-2002 s. 7.4.1-3. 4
Resistance to impact (small & large ball) Class IC2 (F-12N / H-1,6m) EN 13329-F: 2009 3
Heated pan test no changes (aludisk 10 min /185°C) ANSI Z124.6-2007 s.5.6. 1
JC 908-2002 s. 7.9 4
High temperature resistance no changes ( 24 h / hot wax) NEMA LD 3: 2005 -3.6 1
JC 908-2002 s. 7.10D 4
Humid climate resistance no changes (14 Days, 40°C, 85% H) 2 PfG 2507 – 1 2
Alternating climate resistance no changes (-20°C – +60°C) 2 PfG 2507 – 2 2
Dimension deviation 0,13 mm / m pass (max 1,50 mm/m) JC 908-2002 s. 7.1. 4
Behaviour in dry heat Class 7C 180°C (DIN 68861- 7, 2001-04 ) DIN EN 12722 2
Behaviour in wet heat Class 8A 100°C (DIN 68861-8, 2001-04 ) DIN EN 12721 2
Vapourization with water no changes AMK MB-005.1 2015 2
Water resistance pass JC 908-2002 s.7.11. 4
Abrasion resistance Class 2A > 650 rotations ( DIN 68861-2, 2013-02) DIN EN 15185 2
Graphite test no changes (Test with pencil 6HB) DIN EN 12720 2
Cigarette test pass JC 908-2002 s.7.7.1. 4

1 SGS-CSTC – Test report GZCCM140200158 dtd 2014
2 TÜV Rheinland – Test report 21255145_001 dtd 2016
3 TÜV Rheinland – Test report 21245130_002 dtd 2016
4 SGS-CSTC – Test report GZCCM130300183-03 dtd 2013
5TÜV Rheinland – Test report 21250279_001 dtd 2016
6Test made by Akrilika

BEHAVIOUR AT CHEMICAL INFLUENCE – APIETRA

3. Test according to DIN 68861-11

Test substrates Requirements acc. DIN EN 12720
Reagents, 1 Cl 1A -MAX 1B 1C-MIN Results /
Acetic acid 16h 5 1h 5 1A5 ok
Citric acid 16h 5 1h 5 1A5 ok
Ammonia solution 16h 5 2min 5 1A5 ok
Ethylene alcohol 16h 5 1h 4 1A5 ok
Red wine 16h 5 6h 5 10min 5 1A5 ok
Beer 16h 5 6h 5 10min 5 1A5 ok
Cola beverage 16h 5 16h 5 10min 5 1A5 ok
Coffee 16h 5 16h 5 10min 5 1C5-1A5 ok
Black tea 16h 5 16h 5 10min 5 1A5 ok
Black current juice 16h 5 16h 5 10min 5 1A5 ok
Condensed milk 16h 5 16h 5 10min 5 1C5-1A5 ok
Petrol 16h 5 2min 5 1A5 ok
Acetone 16h 5 10s 2 1B5-1A5 ok
Ethylen-butylene acetate 16h 5 10s 2 1B5-1A5 ok
Olive oil 16h 5 16h 5 1A4-1A5 ok
Mustard 16h 5 6h 5 1A3-1A5 ok
Disinfectant 16h 5 10min 5 2min 5 1A5 ok
Black ballpoint ink 16h 5 1A2 ok
Stamp pad ink 16h 5 1A3 ok
Detergent 16h 5 1h 5 1B5-1A5 ok
Detergent solution 16h 5 1h 5 2min 5 1A5 ok

5 – no change, 4 – minor change, 3-moderate change, 2- significant change
1 TÜV Rheinland – Test report 21255144_000 dtd 2016

4. Test according to ISO 19712-2 p102

Test substrates Requirements acc. ISO 19712-2 p10 (A)
MAX NORM MIN Results
Coffee 5 4 3 4 ok
Natronlauge, 25% 5 4 3 5 ok
H-peroxid, 30% 5 4 3 5 ok
Acetone 5 4 3 3 ok
Black shoe cream 5 4 3 4 ok
Citric acid, 10% 5 4 3 5 ok

2 TÜV Rheinland – Test report 21245130_002 dtd 2016

5. Test according to ANSI Z124.6-20073

Stain resistance Requirements acc. ANSI Z124.3-2005
Test substrates T MAX-MIN max depth Results
Black crayon 16h 1 5 0,127mm 2 2 0 mm pass
Black shoe polish 16h 1 5 0,127mm 1 1 0 mm pass
Blue washable ink 16h 1 5 0,127mm 5 3 0,025 mm pass
Gentian violet solution 16h 1 5 0,127mm 5 3 0,025 mm pass
Iodine solution, 1% 16h 1 5 0,127mm 5 2 0,025 mm pass
Lipstick 16h 1 5 0,127mm 2 2 0 mm pass
Beet juice 16h 1 5 0,127mm 1 1 0 mm pass
Grape juice 16h 1 5 0,127mm 2 1 0 mm pass
Wet tea bag 16h 1 5 0,127mm 1 1 0 mm pass
Hair dye 16h 1 5 0,127mm 4 3 0 mm pass
Chemical resistance Requirements acc. ANSI Z124.6-2007
Test substrates T Results
Naphtha 16h no changes pass
Ethyl alcohol 16h no changes pass
Amyl acetate 16h no changes pass
Ammonia solution, 10% 16h no changes pass
Citric acid, 10% 16h no changes pass
Urea, 6% 16h no changes pass
Hydrogen peroxide solution, 3% 16h no changes pass
Concentr. sodium hypochlorite solution 16h no changes pass
Toluene 16h no changes pass
Ethyl acetate 16h no changes pass
Lye solution, 2% 16h no changes pass
Acetone 16h no changes pass
Trisodium phosphate (5: 95 Water) 16h no changes pass
Vinegar 16h no changes pass
Pine oil 16h no changes pass

3 SGS-CSTC – Test report GZCCM140200158 dtd 2014

FOOD SAFETY TESTS – APIETRA

6. Food safety tests

Test Results Norms *
Sensory analysis, smell/taste
(H2O)
pass LFGB, § 31-1, DIN 10955
Reg EU 1935/2014 -3.
1
Migration of Acrylonitril, formaldehyde, Metals (Ba, Co, Cu, Fe, Li, Mn, Zn), PAA, PAHs, 8 EU-PAHs, acrylic and methacrylic acid pass Reg EU 10/2011
Reg EU 1907/2006
DIN EN 13130
1
Color migration of pigmented plastics pass BfR-IX, Resolution AP (89) 1 1

1 TÜV Rheinland – Test report 0003162423/40 AZ227041 dtd 2016